Temperature and pressure dependence of electrical conductivity in synthetic anorthite
Haiying Hu; Lidong Dai; Heping Li; Keshi Hui; Jia Li
2015
Source PublicationSolid State Ionics
Volume276Issue:1Pages:136-141
AbstractElectrical conductivity measurements of synthetic anorthite were carried out as a function of pressure and temperature by a Solartron-1260 Impedance/Gain phase analyzer in a multi-anvil apparatus. The impedance spectroscopy was performed in a frequency range from 10-1 Hz to 106 Hz. The sample was synthesized at 1673 K in a high temperature furnace. Our experimental results show that (1) a dramatic increase in electrical conductivity with increasing temperature and a slightly decrease in conductivity with increasing pressure at constant temperature, however, the effect of pressure on the conductivity is less pronounced than that of temperature; (2) the activation enthalpy linearly increases with increasing pressure (1.86-1.91 eV) reflecting the mobility of Ca2(+) decreases as the anorthite framework becomes more compressed; (3) the activation energy at atmospheric pressure and activation volume are 1.83 eV and 2.39 cm(3)/mol, respectively; (4) According to these Arrhenius parameters, it is proposed that the possible dominant mechanism of the charge transport in anorthite under experimental conditions is the hopping of Ca2(+) from one near aluminum oxygen site to another; (4) the diffusion coefficient of calcium was calculated from the present conductivity data using Nernst-Einstein equation, and compared with previous experimental results.
KeywordAnorthite Electrical Conductivity Transport Mechanism Diffusivity
Subject Area地球深部物质与流体作用地球化学
Indexed BySCI
Language英语
Document Type期刊论文
Identifierhttp://ir.gyig.ac.cn/handle/352002/6034
Collection地球内部物质高温高压实验室_地球内部物质高温高压实验室_期刊论文
Recommended Citation
GB/T 7714
Haiying Hu,Lidong Dai,Heping Li,et al. Temperature and pressure dependence of electrical conductivity in synthetic anorthite[J]. Solid State Ionics,2015,276(1):136-141.
APA Haiying Hu,Lidong Dai,Heping Li,Keshi Hui,&Jia Li.(2015).Temperature and pressure dependence of electrical conductivity in synthetic anorthite.Solid State Ionics,276(1),136-141.
MLA Haiying Hu,et al."Temperature and pressure dependence of electrical conductivity in synthetic anorthite".Solid State Ionics 276.1(2015):136-141.
Files in This Item:
File Name/Size DocType Version Access License
Temperature and pres(646KB) 开放获取LicenseView Application Full Text
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Haiying Hu]'s Articles
[Lidong Dai]'s Articles
[Heping Li]'s Articles
Baidu academic
Similar articles in Baidu academic
[Haiying Hu]'s Articles
[Lidong Dai]'s Articles
[Heping Li]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Haiying Hu]'s Articles
[Lidong Dai]'s Articles
[Heping Li]'s Articles
Terms of Use
No data!
Social Bookmark/Share
File name: Temperature and pressure dependence of electrical conductivity in synthetic anorthite.pdf
Format: Adobe PDF
This file does not support browsing at this time
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.