Raman scattering of 2H-MoS2 at simultaneous high temperature and high pressure (up to 600 K and 18.5 GPa) | |
JianJun Jiang; HePing Li; LiDong Dai; HaiYing Hu; ChaoShuai Zhao | |
2016 | |
发表期刊 | AIP Advances |
卷号 | 6期号:3 |
摘要 | The Raman spectroscopy of natural molybdenite powder was investigated at simultaneous conditions of high temperature and high pressure in a heatable diamond anvil cell(DAC), to obtain the temperature and pressure dependence of the main Raman vibrational modes (E1g,E12g,A1g, and 2LA(M)). Over our experimental temperature and pressure range (300–600 K and 1 atm−18.5 GPa), the Raman modes follow a systematic blue shift with increasing pressure, and red shift with increasing temperature. The results were calculated by three-variable linear fitting. The mutual correlation index of temperature and pressure indicates that the pressure may reduce the temperature dependence of Raman modes. New Raman bands due to structural changes emerged at about 3–4 GPa lower than seen in previous studies; this may be caused by differences in the pressure hydrostaticity and shear stress in the sample cell that promote the interlayer sliding. |
学科领域 | 地球深部物质与流体作用地球化学 |
收录类别 | SCI |
语种 | 英语 |
文献类型 | 期刊论文 |
条目标识符 | http://ir.gyig.ac.cn/handle/352002/6165 |
专题 | 地球内部物质高温高压实验室_地球内部物质高温高压实验室_期刊论文 |
推荐引用方式 GB/T 7714 | JianJun Jiang,HePing Li,LiDong Dai,et al. Raman scattering of 2H-MoS2 at simultaneous high temperature and high pressure (up to 600 K and 18.5 GPa)[J]. AIP Advances,2016,6(3). |
APA | JianJun Jiang,HePing Li,LiDong Dai,HaiYing Hu,&ChaoShuai Zhao.(2016).Raman scattering of 2H-MoS2 at simultaneous high temperature and high pressure (up to 600 K and 18.5 GPa).AIP Advances,6(3). |
MLA | JianJun Jiang,et al."Raman scattering of 2H-MoS2 at simultaneous high temperature and high pressure (up to 600 K and 18.5 GPa)".AIP Advances 6.3(2016). |
条目包含的文件 | ||||||
文件名称/大小 | 文献类型 | 版本类型 | 开放类型 | 使用许可 | ||
Raman scattering of (1484KB) | 开放获取 | 使用许可 | 浏览 请求全文 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论